Home > Support > Structure and application of the bearings

Structure and application of the bearings

Structure bearings

TYB solid lubricant bearings are produced based on the high-intensity bronze alloy with orderly arranged pores of appropriate size to contain solid lubricants.

This kind of bearing have good wear resistance, low friction, work without any oil for long period. It widely applies in the water conservancy project machinery, like dam gate bushes, tightening pulley sliding bearing, hydraulic turbine bushes, contruction machinery, bridge, chemical industry, metallurgy, petroleum, ship and has become the stereotypia product in each kind of project machinery. To meet the requirments of the customers and to suit more applications. Our company developed with the substrate material bearing for selected.

Civil Projection

Suitable for medical machines, textile machines and sport machines, transportation machines, transmission equipments, electronic products and agriculture industries, etc. As a result of this products fine material behavior, decided the TYB product suited the more used situation, is better than other similar products.

The performance of the bronze alloy

TYB Standard TYB-1 Strong cast bronze TYB-2 strong cast bronze TYB-3 strong cast bronze
Cu% 65 65 65
Zn% 25 25 25
Al% 6 6 6
Mn% 4 4 4
Hardness HB ≥ 210 ≥ 250 ≥ 290
Tensile strength N/mm2 > 750 > 800 > 500
Elongation % > 12 > 4 > 0.5
Max. Load N/mm2 100 150 200
Max. Speed m/min 60 15 10
300N/mm2 < 0.01 < 0.005 < 0.002

Metallurgical structure of the high-strength copper

The high strength copper belongs to α&β' bidirectional copper . Its intensity and hardness is very higher. They are widely used for to manufacture the high strength structural element, with machine in axel sleeve and slide.

Metallurgical structure of the high-strength copper

Wearing and abrasion performance of the bearings

  • Dimension: ø40 x ø50 x L30
  • Hardness: > 210HB
  • Glide speed: V=1.0m/min(0.0166m/s)
  • Unit Pressure: P=250Kgf/cm2(24.5N/mm2
  • Swing angle:α=90°(±45°)
  • Symmetry axis:45#HRC42-45R 0.8
  • Test timeL: 50 hour
  • Lubrication:Dry